XYLAN 1014/P01931E DEEP MED. BLUE #524
APPLICATION INFORMATION:
This product is designed primarily for spray application. Consult with a Whitford representative if
other types of application are being considered. Use an air spray gun with a siphon cup or pressure
pot. Select a fluid nozzle and air cap that meet application needs. The Whitford Laboratory uses a
Binks Model 2001 gun with a #66S fluid nozzle and a #66SD air cap. The air supply line must be
equipped with traps to remove water and oil. Drain and service traps frequently.
Apply the dry film thickness as specified. The proper amount of coating should be achieved with two
or three passes of the spray gun across the work piece. Apply the coating to a uniform, full wet
appearance.
DRY FILM THICKNESS: 0.6 – 1.0 MIL (15 - 25 MICRONS)
CLEAN UP SOLVENT: NMP/XYLENE - 2:1
CURING THE COATING:
In order to completely cure the coating, the SUBSTRATE TEMPERATURE must remain at the
specified temperature for the entire bake schedule.
FLASH OR AIR DRY: 1-2 MINUTES AT 150-175°F (65-80°C) OPTIONAL BUT MAY AID TO
REDUCE SOLVENT POPPING ON LOW MASS PARTS.
BAKE SCHEDULE: 10 MINS AT 450°F (232°C) STANDARD; 10 MINS AT 525°F (275°C)
FOR CHEMICAL RESISTANCE; 10 MINS AT 650°F (343°C) FOR
RELEASE
APPLICATION INFORMATION:
This product is designed primarily for spray application. Consult with a Whitford representative if
other types of application are being considered. Use an air spray gun with a siphon cup or pressure
pot. Select a fluid nozzle and air cap that meet application needs. The Whitford Laboratory uses a
Binks Model 2001 gun with a #66S fluid nozzle and a #66SD air cap. The air supply line must be
equipped with traps to remove water and oil. Drain and service traps frequently.
Apply the dry film thickness as specified. The proper amount of coating should be achieved with two
or three passes of the spray gun across the work piece. Apply the coating to a uniform, full wet
appearance.
DRY FILM THICKNESS: 0.6 – 1.0 MIL (15 - 25 MICRONS)
CLEAN UP SOLVENT: NMP/XYLENE - 2:1
CURING THE COATING:
In order to completely cure the coating, the SUBSTRATE TEMPERATURE must remain at the
specified temperature for the entire bake schedule.
FLASH OR AIR DRY: 1-2 MINUTES AT 150-175°F (65-80°C) OPTIONAL BUT MAY AID TO
REDUCE SOLVENT POPPING ON LOW MASS PARTS.
BAKE SCHEDULE: 10 MINS AT 450°F (232°C) STANDARD; 10 MINS AT 525°F (275°C)
FOR CHEMICAL RESISTANCE; 10 MINS AT 650°F (343°C) FOR
RELEASE